SCHULAFORM® 9 A TF 10
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4Bvrqg_SCHULAFORM-9-A-TF-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% PTFE modified polyoxymethylene |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 7.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 135 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 57.0 | MPa | |
| Break | 56.0 | MPa | |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 91 | kJ/m² | |
| 23°C | 95 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 98.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 163 | °C | ISO 306/A50 |
| -- | 142 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 625 | °C | |
| 3.00 mm | 625 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 650 | °C | |
| 3.00 mm | 650 | °C | |
| Flammability | 26 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2207 TFE 10 | RTP Company | PEEK | RTP |
| Sylvin 7868-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| XANTAR® F 25 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| UMG ABS® FV700G4 | UMG ABS, Ltd. | ABS | UMG ABS® |
| ADDINYL C2 V40 | ADDIPLAST | Nylon 66/6 | ADDINYL |