Shinko-Lac® ABS 1002
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4BUDSh_Shinko-Lac-ABS-1002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS 1002 is a standard grade of ABS that features a high modulus along with an excellent balance of rigidity, strength, processability and glossiness. Typical applications of 1002 include communications equipment, clock accessories, trays and toys. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2750 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 51.0 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2840 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 81.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 39 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 59 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 93.0 | °C | ASTM D648 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GFX1356-BK01 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| ALTECH® PS-HI A 1000/100 | ALBIS PLASTIC GmbH | PS (HIPS) | ALTECH® PS-HI |
| Auracell® H2 | Rotuba Extruders, Inc. | CA | Auracell® |
| Zytel® HTN 53C40HSL BK544 | DuPont Performance Polymers | HPPA | Zytel® HTN |
| Sylvin 8027-65 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |