Pearlbond™ DIPP-119
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlbond™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4BQLOF_Pearlbond-DIPP-119.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlcoat® DIPP-119 is polycaprolactone copolyester based thermoplastic polyurethane, supplied in form of translucent pellets. Featuring low melting point and excellent transparency, this product offers excellent flexibility, elasticity and easy processing. Ideally used for extrusion or compounding with PVC. Pearlcoat® DIPP-119 is used mostly in extrusion applications where low melting point as well as improved adhesion over polar substrates is highly appreciated. It is ideal for PVC compounding. It is also used in solvent coatings on textile substrates. Pearlcoat® DIPP-119 is soluble in MEK, DMF and THF. Diluents such as cyclohexanone and toluene can be added. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| 20°C | 1.16 | g/cm³ | ISO 2781 |
| Moisture Content | < 1000 | ppm | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 45.0 | mm³ | ISO 4649 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 25:1 | ||
| Extruder Screw Compression Ratio | 3:1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 3.00 | MPa | ASTM D412, ISO 527 |
| 300% strain | 4.00 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 750 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 50.0 | kN/m | ASTM D624 |
| -- | 50 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -30.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 118 - 128 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 125 - 135 | °C | |
| Cylinder Zone 2 Temp. | 150 - 160 | °C | |
| Cylinder Zone 3 Temp. | 165 - 175 | °C | |
| Cylinder Zone 4 Temp. | 170 - 180 | °C | |
| Die Temperature | 150 - 160 | °C |
| Extrusion instructions |
|---|
| Cooling: AirSpeed: 50 rpmThickness Die: 0.2 mm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GERMAMID 6 KSZ | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| ENFLEX S3060A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| GXL 10009-X47 | S&E Specialty Polymers, LLC | TPO (POE) | GXL |
| INEOS HDPE B54-25H-127 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| EPAMOULD 755D15 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPAMOULD |