CYCOLOY™ XCY620 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4AxyhM_CYCOLOY-XCY620-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 22 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Break 3 | 52.0 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 4.5 | % | ISO 527-2/50 |
| Break 5 | 120 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 83.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 89.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 9 | 45 | kJ/m² | ISO 179/1eA |
| 23°C 10 | 70 | kJ/m² | ISO 179/1eA |
| 23°C 11 | 60 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 480 | J/m | ASTM D256 |
| 23°C | 640 | J/m | ASTM D256 |
| -30°C 12 | 45 | kJ/m² | ISO 180/1A |
| 23°C 13 | 55 | kJ/m² | ISO 180/1A |
| 23°C 14 | 70 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 70.0 | J | |
| 23°C, Total Energy | 56.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 15 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 107 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 16 | 105 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 127 | °C | ASTM D1525, ISO 306/B50 12 17 |
| -- | 129 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 35 | kV/mm | |
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Oil | 17 | kV/mm |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 195 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 105 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 250 to 290 | °C | |
| Nozzle Temperature | 240 to 280 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*3 |
| 13 . | 80*10*4 |
| 14 . | 80*10*3 |
| 15 . | 80*10*4 mm |
| 16 . | 80*10*4 mm |
| 17 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6003-45A MD NATURAL | RTP Company | TPE | RTP |
| Sumitomo Phenolic FM 21386 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| DELPET™ SR6500 | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| Gallonprene® GP410-8001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LEXAN™ HP9NR resin | SABIC Innovative Plastics | PC | LEXAN™ |