Orevac® 18302N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Arkema |
| Trademark: | Orevac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4AnCe7_Orevac-18302N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OREVAC® 18302N is a maleic anhydride modified low-density polyethylene available in pellet form. It can be processed on most extrusion equipments designed to process conventional polyolefin. Applications: OREVAC® 18302N has been designed to develop a reliable bonding strength between polyethylene or most ethylene copolymers and many kinds of different materials among which polyamides and EVOH. OREVAC® 18302N is also recommended in non-halogen flame retardant cable compounds using high loadings of mineral fillers which require outstanding mechanical properties - high tensile strength at break and good elongation and good chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.912 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield, Compression Molded | 7.00 | MPa | |
| Break, Compression Molded | 20.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 790 | % | ASTM D638, ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 1 | 84.0 | °C | ISO 306/A, ASTM D1525 2 |
| Melting Temperature | 123 | °C | ISO 11357 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 to 180 | °C | |
| Cylinder Zone 2 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 200 to 220 | °C | |
| Cylinder Zone 4 Temp. | 210 to 230 | °C | |
| Cylinder Zone 5 Temp. | 215 to 230 | °C | |
| Adapter Temperature | 220 to 230 | °C | |
| Melt Temperature | > 210 | °C | |
| Die Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | On compression molded samples |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPC-20T Black | PolyOne Corporation | PP Copolymer | Maxxam™ |
| TAROLOX 10 K6 | Taro Plast S.p.A. | PBT | TAROLOX |
| apilon 52® DE 50 | API SpA | TPU-Polyester | apilon 52® |
| INSTRUC PFAGF20 | Infinity LTL Engineered Compounds | PFA | INSTRUC |
| LNP™ COLORCOMP™ D1000P compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |