SPESIN® KP213G15HI
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | SPESIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4AGItG_SPESIN-KP213G15HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SPESIN® KP213G15HI is a Polybutylene Terephthalate (PBT) product filled with 15% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 1.1 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 88.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 7.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 155 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| Peak Melting Temperature | 224 | °C | ASTM D3418 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPELIN® 7111S | MOL Petrochemicals Co. Ltd. | HDPE | TIPELIN® |
| Vydyne® 909 | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| ANYPOL CL-3000F | SH Energy & Chemical | PS (EPS) | ANYPOL |
| AvaSpire® AV-630 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| Karina COMP. PVC BRANCO -E 703D10/ 58-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |