Panlite® LN-3520ZH
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4ADng7_PanliteLN3520ZH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame resistant grade, Non-bromine/non-phosphor type |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Transverse flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 66.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2340 | MPa | ISO 178 |
| Flexural Stress 2 | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 141 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 127 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec (1.5 mm) | 130 | °C | UL 746 |
| RTI Imp (1.5 mm) | 125 | °C | UL 746 |
| RTI (1.5 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.10 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 9.0E-3 | IEC 60250 | |
| 1 MHz | 9.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.0 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm | 930 | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.0 mm | 850 | °C | IEC 60695-2-13 |
| 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6240 B109 | Spartech Polycom | PP Copolymer | Spartech |
| Network Polymers PP PPB 25 0616 BLACK | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Evoprene™ GC 5683 | AlphaGary | SEBS | Evoprene™ GC |
| Epolene® E-43P | Westlake Chemical Corporation | PP, Unspecified | Epolene® |
| LNP™ STAT-KON™ DEL329EP compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |