Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ CL001I compound
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 46K3R8_LNPLUBRICOMPCL001Icompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP CL001I is a compound based on Polystyrene resin containing PTFE. Added features of this material include: Internally Lubricated, High Impact. Also known as: LNP* LUBRICOMP* Compound CL-4010 HI Product reorder name: CL001I |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1850 | MPa | ASTM D638 |
| Tensile Strength (Break) | 20.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 37 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 34.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 72.8 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 513 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| NILENE® E12 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Di-Pak™ E-4566 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Fiberfil® M-2500 BK | Fiberfil® Engineered Plastics Inc. | Nylon 6 | Fiberfil® |
| Flexalloy® OR 9900-60 | Teknor Apex Company | PVC Elastomer | Flexalloy® |