HONES® PBT GT20
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Guangdong Shunde Hones Polymer Material Co., Ltd. |
| Trademark: | HONES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 44YrRh_HONES-PBT-GT20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Technology characteristics: Mineral glass filled, flame retardant, anti-smooth surface warping, high electrical performance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 67.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179 |
| Unnotched Izod Impact (3.20 mm) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 1290/1291 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| Formolene FORMAX® L71709A | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |
| LNP™ THERMOCOMP™ JF004RXP compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |
| Hifax HSBMCB1158ACLS/3 | LyondellBasell Industries | TPO (POE) | Hifax |
| POCAN® B 1600 000000 | LANXESS GmbH | PBT | POCAN® |