RTP ESD A 100 MF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 43dYDr_RTP-ESD-A-100-MF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ESD Protection - Static Dissipative - Medium MFR |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1030 | MPa | ASTM D638 |
| Tensile Strength | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Flexural Strength | 31.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | No Break | ASTM D256 | |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+5 to 9.9E+11 | ohms | ASTM D257 |
| -- | 1.0E+4 to 9.9E+10 | ohms | ESD STM11.11 |
| Volume Resistivity | 1.0E+3 to 9.9E+9 | ohms·cm | ASTM D257 |
| Static Decay 1 | < 2.0 | sec | FTMS 101C 4046.1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMACOR™ 3340 | The Dow Chemical Company | EAA | PRIMACOR™ |
| Badamid® B70 | Bada AG | Nylon 6 | Badamid® |
| FHR Polypropylene P4G3Z-039 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Karina BLACK PVC COMPOUND 780-48/ 1-C-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9424-95 NATURAL | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |