LNP™ STAT-KON™ DX11408 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 42fwPK_LNP-STAT-KON-DX11408-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* DX11408 is a compound based on Polycarbonate containing Carbon Powder. Added features of this material include: Electrically Conductive, Improved Ductility Also known as: LNP* STAT-KON* Compound DX11408 Product reorder name: DX11408 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 1.0 | % | |
| Across Flow : 24 hr | 0.90 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.12 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2590 | MPa | ASTM D638 |
| -- | 2640 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 56.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Break 3 | 48.0 | MPa | ASTM D638 |
| Break | 48.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 4.6 | % | ISO 527-2/5 |
| Break 5 | 22 | % | ASTM D638 |
| Break | 16 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2680 | MPa | ASTM D790 |
| -- 7 | 2480 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 340 | J/m | ASTM D256 |
| 23°C 8 | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 940 | J/m | ASTM D4812 |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 38.6 | J | ASTM D3763 |
| -- | 34.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 127 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8764-65 White 184 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEO-ZEX™ 0234H | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| 3M™ Dyneon™ PTFE Compound TF 6406 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| MAJ'ECO DEN060LA | AD majoris | Biodeg Polymers | MAJ'ECO |
| THERMOLAST® K TF5ADN (Series: FC/AD1/PS) | KRAIBURG TPE | TPE | THERMOLAST® K |