LUVOCOM® 6-7834 VP Datasheet,Nylon 12,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®6-7834 VP is a polyamide 12 (nylon 12) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main characteristics of 6-7834 VP are: Good dimensional stability moisture resistance Lubrication Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies Handle

General Information
Additive	Lubricant
Features	Good dimensional stability Lubrication Low or no water absorption
Uses	Handle Textile applications Engineering accessories Machine/mechanical parts Application in Automobile Field Business equipment Bearing
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.22	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (235°C/5.0 kg)	< 10.0	cm³/10min	ISO 1133
Molding Shrinkage	0.80 - 1.1	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2800	MPa	ISO 527-2
Tensile Stress (Break)	53.0	MPa	ISO 527-2
Tensile Strain (Yield)	5.5	%	ISO 527-2
Flexural Modulus	2300	MPa	ISO 178
Flexural Stress	75.0	MPa	ISO 178
Flexural Strain at Flexural Strength	7.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	140	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+9	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	130	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	90.0	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+9	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
A	75.0	°C
B	105	°C
Drying time- A	6.0 - 10	hr
Suggested Max Moisture	0.10	%
Rear Temperature	230 - 250	°C
Middle Temperature	240 - 260	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 260	°C
Processing (Melt) Temp	250	°C
Mold Temperature	70.0 - 110	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 12 , Polyamide 12
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	42cb2x_LUVOCOM-6-7834-VP.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene HP521-231UV	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
RTP 1001 FR A	RTP Company	PBT	RTP
TRIMID® N66-G43L	Polymer Technology and Services, LLC	Nylon 66	TRIMID®
Geon™ Vinyl Flexible G92C	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
ULTEM™ AUT230 resin	SABIC Innovative Plastics	PEI	ULTEM™