Order Products : sales@su-jiao.com

KPOL-HDPE HD K-0.30/960

Category:	HDPE , High Density Polyethylene
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	42OUML_KPOL-HDPE-HD-K-0-30-960.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Density Polyethylene Homopolymer Extrusion-Blow Molding

Characteristics

The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

Applications

Blow Molded Small Volume: Dairy bottles, yogurt, liquid foods (milk, water, juice) packing and Toys.

General Information
Additive	Antioxidant (250 to 500 ppm)
Features	Antioxidant Food Contact Acceptable High Density Homopolymer
Uses	Beverage Containers Blow Molding Applications Bottles Food Containers Fruit Juice Bottles Toys
Agency Ratings	FDA 21 CFR 177.1520(c)
Processing Method	Blow Molding Extrusion Extrusion Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	0.960	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.30	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
50°C, 3.18 mm, 100% Igepal CO-630, F50	12.0 to 18.0	hr	ASTM D1693A
50°C, 1.91 mm, 100% Igepal CO-630, F50	6.00 to 8.00	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec, 23°C)	50		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	29.0	MPa	ASTM D638
Tensile Elongation ²(Break)	> 300	%	ASTM D638
Flexural Modulus - Tangent ³(3.20 mm)	1650	MPa	ASTM D790B

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	84.1	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ⁴(0.45 MPa, Unannealed)	75.0	°C	ASTM D648
Brittleness Temperature ⁵	< -58.0	°C	ASTM D746A
Vicat Softening Temperature	125	°C	ASTM D1525 ⁶

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	13 mm/min
4 .	2°C/min
5 .	F50; 25 lbfXin
6 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
RABALON® QE128ATH	Mitsubishi Chemical Performance Polymers, Inc.	TPE	RABALON®
AZDEL™ C321-B01	Azdel, Inc.	PP, Unspecified	AZDEL™
Karina WHITE PVC COMPOUND 750D10/ 1-DY-AC	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 7833-85 Yellow 4203	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LNP™ LUBRICOMP™ CL001I compound	SABIC Innovative Plastics	PS (HIPS)	LNP™ LUBRICOMP™