Pomalux® SD-A
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Westlake Plastics Company |
| Trademark: | Pomalux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 40pbGu_Pomalux-SD-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pomalux SD-A (Static-dissipative acetal copolymer) Non-carbon-filled, permanently staticdissipative material which is non-migratory and non-humidity dependent. With enhanced lubricity, Pomalux SD-A provides superior wear resistance and ease of machining. Its extremely low outgassing values and non-sloughing characteristics make it ideal for applications where particulate generation cannot be tolerated. Enhanced lubricity, chemically resistant, and dimensionally stable. Advantages:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 2.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 76 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 42.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 1790 | MPa | ASTM D790 |
| Flexural Strength | 59.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 156 | °C | |
| 1.8 MPa, Unannealed | 88.9 | °C | |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 to 1.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+8 to 1.0E+10 | ohms·cm | ASTM D257 |
| Static Decay - 15% RH | < 0.2 | sec | MIL B-81705 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.762 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9519H | Chevron Phillips Chemical Company LLC | HDPE, HMW | Marlex® |
| Crastin® FG6130 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| INSTRUC PA610GF10 | Infinity LTL Engineered Compounds | Nylon 610 | INSTRUC |
| Lucky Enpla LGF5408A | Lucky Enpla Co LTD | Nylon 66 | Lucky Enpla |
| LUVOCOM® 1-8068/GY VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |