Telcar® TELC 1000-92 UV-2 BLACK 550
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 40geiq_Telcar-TELC-1000-92-UV-2-BLACK-550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar®TELC 1000-92 UV-2 BLACK 550 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Telcar®The typical application fields of TELC 1000-92 UV-2 BLACK 550 are: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 180°C, 30 minutes | 1.3 | % | ASTM D955 |
| 24 hours | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 42 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 290 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain | 8.41 | MPa | ASTM D412 |
| 300% strain | 8.55 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Yield 2 | 10.3 | MPa | ASTM D412 |
| Yield 3 | 7.58 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Yield 4 | 16 | % | ASTM D412 |
| Fracture 5 | 540 | % | ASTM D412 |
| Fracture 6 | 140 | % | ASTM D412 |
| Tear Strength 7 | 364 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-40°C) | No Break | ASTM D256 | |
| Dart Drop Impact (-30°C) | 33.9 | J | ASTM D3029 |
| Tensile Impact Strength | 471 | kJ/m² | ASTM D1822 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D573 | ||
| -- | 6.0 | % | ASTM D573 |
| 110°C, 1008 hr | 10 | % | ASTM D573 |
| 121°C, 1008 hr | 7.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | ASTM D573 | ||
| 110°C, 1008 hr | -67 | % | ASTM D573 |
| 121°C, 1008 hr | -63 | % | ASTM D573 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 62.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 40.6 | °C | ASTM D648 |
| Glass Transition Temperature | -55.9 | °C | ASTM E1356 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Lateral | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 30 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Instrumented Dart Impact Energy @ Yield, -40°C, 9000 in/min, Ductile Failure: 200 in-lbsInstrumented Dart Impact Deflection @ Break, -40°C, 9000 in/min, Ductile Failure: 1359 milsInstrumented Dart Impact Energy @ Break, -40°C, 9000 in/min, Ductile Failure: 350 in-lbsFogging, Kaake Buchler, 3 hrs, 100°C: 92Tear Strength, ASTM D1004, Die C: 364 lb/inHeat Aging Performance Izod Impact, 1000 hrs, 120°C: No BreakTensile Impact Strength, ASTM D1822: >224 ft-lb/in²Flammability, Burn Rate, FMVSS 302, Max 100, 30.2 mm/min: PassFlammability, Burn Rate, FMVSS 302, Max 100, 1.2 in/min: Pass |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | Type 1, 510mm/min |
| 5 . | 51 mm/min |
| 6 . | 510 mm/min |
| 7 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ RC66G33-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| TRIMID® N66-1010 | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| ISORENE™ AA6C2-7001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| KEBAFORM® C 6027 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Sylvin 7833-75 Grey 9280 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |