| Category: | PPA , Polyphthalamide |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 40NXRW_NILAMIDXT4GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
SPECIALTY PPA COMPOUND
PPA, 30% GLASS FIBER REINFORCED, HEAT STABILIZED, DESIGNED FOR IMPROVED CYCLE TIME |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 23°C | 0.70 | % | ISO 294-4 |
| Flow : 23°C | 0.30 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.5 | kJ/m² | ISO 179/1eA |
| 23°C | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 32 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 295 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | °C | IEC 60216 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 21 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.40 mm | HB | UL 94 | |
| 0.8 mm | HB | UL 94 | |
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® SX10G-15 | Toray Resin Company | Nylon 6+ABS | Toyolac® |
| Toraycon® 1101G-30 | Toray Resin Company | PBT | Toraycon® |
| 3M™ Dyneon™ PTFE Compound TF 6404 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Badadur® PBT8 TM-Z3 | Bada AG | PBT | Badadur® |
| Arak HDPE BL4 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |