Ghaed ABS ABS-GH-500
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3zw9iy_Ghaed-ABS-ABS-GH-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Classification: Special grade/ultra high heat resistance Characteristic: Ultra Heat Resistance& No odor Application: Automobile parts and Electronic parts and etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 to 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 44.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 20 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1960 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 66.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5 | > 14 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 107 | °C | ASTM D648 |
| Vicat Softening Temperature | > 120 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 200 to 210 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K8003 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Versaflex™ G 7370 | PolyOne Corporation | TPE | Versaflex™ |
| Andur 8500 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Laprene® 8ST193A80/T2 | SO.F.TER. SPA | SEBS | Laprene® |
| Leona™ MR001 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |