NORYL™ LTA5020 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3yCYsc_NORYL-LTA5020-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL LTA5020 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. NORYL LTA5020 is only available in a dark grey/black and may be an excellent material candidate for application requiring electrically insulating properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.20 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % | |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2850 | MPa | ASTM D638 |
| -- | 2840 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 80.0 | MPa | ASTM D638 |
| Yield | 83.3 | MPa | ISO 527-2/50 |
| Break 3 | 60.0 | MPa | ASTM D638 |
| Break | 80.6 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.8 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 5 | 18 | % | ASTM D638 |
| Break | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2770 | MPa | ASTM D790 |
| -- 7 | 2920 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 132 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 39 | J/m | ASTM D256 |
| 23°C | 90 | J/m | ASTM D256 |
| -30°C 10 | 3.9 | kJ/m² | ISO 180/1A |
| 23°C 11 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| -30°C 12 | 34 | kJ/m² | ISO 180/1U |
| 23°C 13 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 17.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 134 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 112 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 116 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 115 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ASTM D1525, ISO 306/B120 11 15 |
| -- | 135 | °C | ISO 306/B50 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 135°C 16 | Pass | ||
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.9E-5 | cm/cm/°C | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.2E+14 | ohms | ASTM D257 |
| Volume Resistivity | 3.7E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 30 | kV/mm | |
| 3.20 mm, in Oil | 19 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.87 | ||
| 60 Hz | 2.87 | ||
| 1 MHz | 2.76 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 0.025 | ||
| 60 Hz | 0.025 | ||
| 1 MHz | 3.0E-3 | ||
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-0 | ||
| 3.00 mm, Testing by SABIC | 5VA | ||
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 800 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Nozzle Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| 16 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4607 HI FR | RTP Company | SPS | RTP |
| Sinvicomp SIM4009 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Fainplast PVC MPH 62/Y | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Durez® 29502 B | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Karina CLEAR PVC COMPOUND 80/203-D-ATD-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |