VALOX™ V4860HR resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3xmgGb_VALOX-V4860HR-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 12.4 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 1.0 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.19 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9750 | MPa | ASTM D638 |
| -- | 9450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 116 | MPa | ASTM D638 |
| Yield | 112 | MPa | ISO 527-2/5 |
| Break 3 | 115 | MPa | ASTM D638 |
| Break | 111 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.3 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2/5 |
| Break 5 | 2.3 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6740 | MPa | ASTM D790 |
| -- 7 | 7880 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 182 | MPa | ISO 178 |
| -- | 183 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 174 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 2.96 | MPa | ASTM D790 |
| Flexural Strain at Break 10 | 2.9 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 74 | J/m | ASTM D256 |
| 23°C | 90 | J/m | ASTM D256 |
| -30°C 12 | 8.5 | kJ/m² | ISO 180/1A |
| 23°C 13 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 13.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 221 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 197 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 188 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 176 | °C | ASTM D1525, ISO 306/B50 12 15 |
| -- | 175 | °C | ISO 306/B120 |
| Ball Pressure Test 16(75°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 95°C | 2.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 95°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Back Pressure | 0.345 to 0.690 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| 16 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6310H | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Toyolac® PX10 X07 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Hylon® N1000EHL2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Petrothene® XL07407 | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |
| Sylvin 8200-93UV Clear Yellow 4194 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |