SCHULAMID® 66 GF 30 GID K1802
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3xmG46_SCHULAMID-66-GF-30-GID-K1802.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre reinforced Polyamide 66, optimized for GID- processes |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9700 | 5700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 175 | 110 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.2 | 8.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 8000 | -- | MPa | ISO 178 |
| Flexural Stress | 250 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 4.7 | -- | % | ISO 178 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability | < 100 | -- | mm/min | FMVSS 302 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1 | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 13 | 19 | kJ/m² | |
| Charpy Unnotched Impact Strength | ||||
| -- | -- | 98 | kJ/m² | ISO 179/1U |
| -30°C | 72 | -- | kJ/m² | ISO 179/1U |
| 23°C | 80 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 242 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | > 250 | -- | °C | ISO 306/A50, ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 650 | -- | °C | |
| 3.00 mm | 675 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 675 | -- | °C | |
| 3.00 mm | 700 | -- | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1160 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Ranger PBT PBT-201-G15 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Fainplast PVC GSK 74/UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Grilamid® L 25A NZ | EMS-GRIVORY | Nylon 12 | Grilamid® |
| ULTEM™ 2200F resin | SABIC Innovative Plastics | PEI | ULTEM™ |