SNOLEN® EP 0.26/51 N
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JSC Gazprom neftekhim Salavat |
| Trademark: | SNOLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3wARFy_SNOLEN-EP-0-26-51-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CHARACTERISTIC PROPERTIES High density polyethylene (HDPE). Extra-high environmental stress crack resistance. High impact strength. High hydrostatic strength for PE 100 pipe grades. UV protection not required. MAJOR APPLICATIONS PE 100 extrusion pipe grades. Process pipes (incl. pressure pipes). Gas pipes. Potable water pipes. Wear plates. Fittings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.947 to 0.951 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 5.2 to 7.2 | g/10 min | |
| 190°C/5.0 kg | 0.20 to 0.26 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(80°C, 2% Arkopal) | 400 | hr | ISO 16770 |
| Melt Flow Ratio | 25.0 to 31.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resistance to Rapid Crack Propagation, Pc - Test S4 | > 20.0 | bar | ISO 13477 |
| Resistance to Slow Crack Growth - Notch Test (SCG) 2 | > 1000 | hr | ISO 13479 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resistance to Internal Pressure - Hydrostatic Strength 3(80°C) | > 2 | yr | ISO 1167 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 850 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 23.0 | MPa | |
| Break | 36.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | |
| Break | > 1000 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | @ 4.0 MPa |
| 2 . | @ 4.6 MPa |
| 3 . | @ 4.6 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 4025 HV | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Delrin® 527UVE RD402 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Geon™ HTX M6220 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| Ketron® PEEK-1000 | Quadrant Engineering Plastic Products | PEEK | Ketron® |
| HiFill® ABS GF10 | Techmer Engineered Solutions | ABS | HiFill® |