NORYL™ IGN320 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3uHafb_NORYL-IGN320-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass reinforced PPE + PS. High heat, high modulus automotive applications like ignition coils. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6260 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 109 | MPa | |
| Break | 109 | MPa | |
| Tensile Elongation 3(Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 5720 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 510 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 16.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 164 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 159 | °C | |
| Vicat Softening Temperature | 175 | °C | ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.60 mm, in Oil) | 34 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 266 to 316 | °C | |
| Middle Temperature | 277 to 321 | °C | |
| Front Temperature | 288 to 327 | °C | |
| Nozzle Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® R123-03 | Razin™ Engineering Plastics | PP, Unspecified | Razalen® |
| RAMSHINE PV3003R2 | Polyram Ram-On Industries | ABS | RAMSHINE |
| Selvol™ E 107 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Hostalen PP H1022 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |
| ISPLEN® PB 176 N4M | REPSOL | PP Impact Copolymer | ISPLEN® |