ASTAMID™ MB3EG6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3u1SIg_ASTAMID-MB3EG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTAMID™ MB3EG6 is a 30% glass reinforced, heat stabilised Polyamide 6 (PA 6 or Nylon 6). Note: The letters "U", "W" or "UV" indicate UV stabilisation has been added [ ie: ASTAMID™ MA3EG5U ]. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | -- | % | ASTM D955 |
| Water Absorption | ||||
| Saturation, 23°C | 6.5 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 9500 | 6200 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 185 | 115 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 4.0 | 8.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 8600 | 5000 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 270 | 190 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 6 | 16 | 30 | kJ/m² | ISO 179 |
| Notched Izod Impact (3.20 mm) | 150 | 210 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | -- | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 210 | -- | °C | |
| CLTE - Flow | 3.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 275 to 285 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFN8510 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Moplen HP652P | LyondellBasell Industries | PP Homopolymer | Moplen |
| Naxel PC524 | Custom Resins Group | PC | Naxel |
| Fortron® CES50 | Celanese Corporation | PPS | Fortron® |
| LEXAN™ HF500R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |