KEBAFORM® C 904 GB
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BARLOG plastics GmbH |
| Trademark: | KEBAFORM® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3siMzh_KEBAFORM-C-904-GB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM Copolymer, 20% glass bead reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.19 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 44.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -H H6410M | TOSOH Corporation | EVA | Melthene® -H |
| Smooth-Cast® 321 | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| 3M™ Dyneon™ PTFE Compound TF 4104 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| LEXAN™ EXL1132 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| PETILEN H5-21T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |