API PS 545
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | American Polymers, Inc. |
| Trademark: | API PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3sGLbd_API-PS-545.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
API 545 is a high impact, high heat resistant grade of impact modified polystyrene. This material features fast set-up as well as easy colorability. Application: API 545 is suggested for heavy parts with large cross section requiring high impact resistance. Housings, tote bins, and shoe heels are some examples. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 47 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1930 | MPa | ASTM D638 |
| Tensile Strength (Break) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 58 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 87.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 177 to 232 | °C | |
| Front Temperature | 191 to 274 | °C | |
| Mold Temperature | -6.67 to 71.1 | °C | |
| Injection Pressure | 34.5 to 276 | MPa | |
| Back Pressure | 0.0689 to 3.45 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravalene CR H 2444 | Ravago Group | HDPE | Ravalene |
| Zythane® 7085AU | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| Fluon® PTFE RB2510 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| SABIC® PPcompound 8650U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| OTECH PVC OE8033 - Calendering | OTECH Corporation | PVC, Unspecified | OTECH PVC |