Sevrene® 3000-60A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Sevrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3s5XU2_Sevrene-3000-60A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sevrene® 3000-60A is a Thermoplastic Elastomer (TPE) material. It is available in North America for coextrusion, extrusion, or injection molding. Primary attribute of Sevrene® 3000-60A: Good Weather Resistance. Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 64 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Across Flow : 100% Strain | 1.80 | MPa | |
| Flow : 100% Strain | 2.50 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Across Flow : Break | 6.60 | MPa | |
| Flow : Break | 4.80 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Across Flow : Break | 1100 | % | |
| Flow : Break | 680 | % | |
| Tear Strength | ASTM D624 | ||
| Across Flow | 28.9 | kN/m | |
| Flow | 25.7 | kN/m |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Fogging (38°C) | 83.1 | SAE J1756 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600/58 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Bergamid™ B70 G30 Black | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Axiall PVC UV-6676 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LubriOne™ PS-30GF/2S Natural | PolyOne Corporation | PBT | LubriOne™ |
| Sylvin 9077-95LMW White 125 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |