KumhoSunny PBT HEB4010
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3rgyF0_KumhoSunny-PBT-HEB4010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEB4010 is a free painting PBT resin, offering high gloss and outstanding appearance, very low haze and excellent processing properties.HEB4010 is recommended for headlight lamp,such as bezel,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 38 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 1.8 to 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 57.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Flexural Stress 2 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(0.45 MPa, Unannealed) | 190 | °C | ISO 75-2/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® MO (500 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Next Nylon 6 Prime Series NGF30-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Clariant Nylon 6/6 PA-111C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Flexus 9211 | Braskem | LLDPE | Flexus |
| Lupox® HV1010 | LG Chem Ltd. | PBT | Lupox® |