PALMID®R 66 S GF 20 is a polyamide 66 (nylon 66) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Typical application areas are: housing. Features include: flame retardant/rated flame Good dimensional stability Good stiffness chemical resistance

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Features	Good dimensional stability Rigid, good Good chemical resistance
Uses	Shell
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.27	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	6.7	%	ISO 62
Equilibrium, 23°C, 50% RH	2.1	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	6800	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	150	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	2.5	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	7.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	50	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	253	°C	ISO 306/B50
Melting Temperature (DSC)	260	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	550	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 6600 to 7000 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 145 to 155 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 45 to 55 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 6 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 250 to 255 °CDensity, ISO 1183: 1.26 to 1.28 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 6.6 to 6.8 %Moisture Absorption, ISO 62, 23°C, 50% RH: 2 to 2.2 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 6600 to 7000 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 145 to 155 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 3 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 45 to 55 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 6 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 250 to 255 °CDensity, ISO 1183: 1.26 to 1.28 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 6.6 to 6.8 %Moisture Absorption, ISO 62, 23°C, 50% RH: 2 to 2.2 %

Category:	Nylon 66 , Polyamide 66
Manufacturer:	pal plast GmbH
Trademark:	PALMID®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3rcTXZ_PALMID-R-66-S-GF-20.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
NITRIFLEX N-689 B	NITRIFLEX	NBR	NITRIFLEX
DAUNYL 66 AV	Daunia Trading srl	Nylon 66	DAUNYL
Edgetek™ CY4000 NC002	PolyOne Corporation	PC+PBT	Edgetek™
Eleme JPRG030	Eleme Petrochemical Company Ltd	PP Homopolymer	Eleme
VALOX™ DR51 resin	SABIC Innovative Plastics	PBT	VALOX™