OmniTech™ ASA 220
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniTech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3rZ7Xv_OmniTech-ASA-220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General Purpose ASA |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (265°C/3.4 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 46.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 96.1 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | < 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 216 to 260 | °C | |
| Nozzle Temperature | 216 to 260 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5010GN6-30M8X | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Daelim Po1y® LH-3250 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Hostaform® S 9243 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Plenco 00755 (Compression) | Plastics Engineering Co. | Mel Phenolic | Plenco |
| Elastollan® 1185 A 15 000 | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |