MAJORIS BG400 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3rS6Gn_MAJORIS-BG400---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BG400 - 8229 is a 40% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. BG 400 - 8229 has been developed especially for the automotive under the bonnet applications. BG 400 - 8229 has very high stiffness, high impact strength, good dimensional stability and good creep resistance also at high temperatures. APPLICATIONS Product requiring high service temperature and extremely high mechanical strength, such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 - 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 95.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 6300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 31 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 149 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 165 | °C | ISO 306/A |
| -- | 137 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G1733H-01A | RheTech, Inc. | Nylon 6 | Rhelon |
| BESTNYL SI50VI02ANU | Triesa Plastics | Nylon 6 | BESTNYL |
| ANYPOL SE-160LL | SH Energy & Chemical | PS (EPS) | ANYPOL |
| DAI-EL™ G-7451 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Karina PINK COLOR CONCENTRATE -E 39/ 87-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |