Apec® 1803

Category:	PC , Polycarbonate
Manufacturer:	Covestro - Polycarbonates
Trademark:	Apec®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3rN5hG_Apec-1803.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
MVR (330°C/2.16kg) 10 cm³/10 min; high viscosity; UV stabilized; 'softening temperature (VST/B 120)=184 °C; injection molding - melt temperature 330 - 340°C; Covers for brake lights and indicator lights; car interior light covers; Domestic lamp covers; Headlamp lenses; Covers for ships' lights; Connector pieces for halogen systems

General Information
Additive	UV Stabilizer
Features	High Viscosity
Uses	Automotive Applications Automotive Backlights Connectors Lighting Applications
RoHS Compliance	RoHS Compliant
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.15	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (330°C/2.16 kg)	10	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (330°C/2.16 kg)	10.0	cm³/10min	ISO 1133
Molding Shrinkage ¹			ISO 294-4
Across Flow : 2.00 mm	0.85	%
Flow : 2.00 mm	0.85	%
Water Absorption			ISO 62
Saturation, 23°C	0.30	%
Equilibrium, 23°C, 50% RH	0.12	%

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	121	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2400	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	72.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C)	6.8	%	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	> 50	%	ISO 527-2/50
Flexural Modulus ²(23°C)	2400	MPa	ISO 178
Flexural Stress ³(23°C)	108	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break
23°C	No Break

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	174	°C	ISO 75-2/B
1.8 MPa, Unannealed	159	°C	ISO 75-2/A
Vicat Softening Temperature	184	°C	ISO 306/B120
CLTE			ISO 11359-2
Flow : 23 to 55°C	6.5E-5	cm/cm/°C
Transverse : 23 to 55°C	6.5E-5	cm/cm/°C
RTI Elec	150	°C	UL 746
RTI Imp	130	°C	UL 746
RTI Str	150	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+16	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+17	ohms·cm	IEC 60093
Electric Strength (23°C, 1.00 mm)	35	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	2.90
23°C, 1 MHz	2.80
Dissipation Factor			IEC 60250
23°C, 100 Hz	1.0E-3
23°C, 1 MHz	8.0E-3
Comparative Tracking Index			IEC 60112
Solution A	450	V
Solution B	100	V

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm)	HB		UL 94
Glow Wire Flammability Index	850	°C	IEC 60695-2-12
Oxygen Index ⁴	25	%	ISO 4589-2

Optical	Nominal Value	Unit	Test Method
Refractive Index ⁵	1.573		ISO 489
Transmittance (1000 µm)	89.0	%	ISO 13468-2

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion (23°C)	A1		IEC 60426

Note Message
1 .	60x60x2 mm
2 .	2.0 mm/min
3 .	2.0 mm/min
4 .	Procedure A
5 .	Method A

Resin Grade	Manufacturer	Category	Trademark
Santoprene™ 121-62M100	ExxonMobil Chemical	TPV	Santoprene™
RheTech Thermoplastic Polyolefin FT1055-01	RheTech, Inc.	Polyolefin, Unspecified	RheTech Thermoplastic Polyolefin
Sylvin 9223-55 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
DJSilicone NE-150	DONGJUE SILICONE (NANJING) CO., LTD	Silicone	DJSilicone
PolyFibra® PF-PEF02	FuturaMat	PP, Unspecified	PolyFibra®