CALIBRE™ 5201-12
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3plZrI_CALIBRE-5201-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 5201-12 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-12 resin is typically used in medical market applications. CALIBRE 5201-12 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5170 | MPa | ASTM D638 |
| -- | 5170 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 82.7 | MPa | ASTM D638 |
| Yield | 82.7 | MPa | ISO 527-2/50 |
| Break 3 | 82.7 | MPa | ASTM D638 |
| Break | 82.7 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 2.6 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2/50 |
| Break 5 | 3.0 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 4830 | MPa | ASTM D790 |
| -- 7 | 4820 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 148 | MPa | ASTM D790 |
| -- 9 | 148 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ASTM D256 |
| Instrumented Dart Impact 10(23°C, 3.20 mm, Total Energy) | 46.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 148 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 138 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 142 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 159 | °C | ASTM D1525 11 |
| -- | 158 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 12 | UL 94 | ||
| 1.59 mm | V-2 | ||
| 3.05 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| 6 . | Method I (3 point load), 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Method I (3 point load), 2.0 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 3.39 m/sec |
| 11 . | Rate A (50°C/h), Loading 2 (50 N) |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SI302G30 | RJM International, Inc. | PET | RJM |
| Shin-Etsu Elastomer KE-931U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| SLOVALEN庐 PC 71 T 10 | Plastcom | PP, Unspecified | SLOVALEN® |
| TATREN® HT 3 06 | Slovnaft Petrochemicals, s.r.o. | PP Homopolymer | TATREN® |
| Galloo GP-ABS-5510 | Galloo Plastics | ABS | Galloo |