EPLAMID 6 IMP NC B801
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3o9eOM_EPLAMID-6-IMP-NC-B801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unreinforced and modified polyamide 6, with improved good-impact resistance, heat stabilized, lubricated for injection molding. Eplamid 6 IMP B801 offers an excellent Notched High Impact resistance with ensures outstanding performance at low temperatures making it suitable for all sectors of industries and for applications such as sports & liesure and automative industries. This material is available in natural and in colours on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.05 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.9 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 1.5 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 75 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | 1850 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 36.0 | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 50 | > 40 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1900 | 1750 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 80.0 | 70.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 70 | 75 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 66 | 70 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature (DSC) | 215 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P256-670UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Adflex X 101 H | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |
| Braskem PP H 118 | Braskem | PP Homopolymer | Braskem PP |
| INLUBE PA66GF30TF15 | Infinity LTL Engineered Compounds | Nylon 66 | INLUBE |
| MAJ'ECO DFRG178G - 1199 | AD majoris | Biodeg Polymers | MAJ'ECO |