POLYLAC® PA-765B
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3mygTY_POLYLAC-PA-765B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC®PA-765B is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| 23°C | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 4.2 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 42 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 45 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 12.7 mm) | 102 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 82.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 3.18mm 1 | 39.1 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/50 |
| Fracture | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture, 3.18mm 2 | 25 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.35 mm 3 | 196 | MPa | ASTM D790 |
| -- 4 | 1800 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 5 | 63.4 | MPa | ASTM D790 |
| -- 6 | 57.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 250 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 220 | J/m | ASTM D256 |
| -- | 20 | kJ/m² | ISO 180/1A |
| Impact Flexural Test - Notched | 13.0 | kJ/m² | ISO 179/2C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.35mm | 76.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 77.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed | 91.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 92.0 | °C | ASTM D1525, ISO 306/A120 6 7 |
| -- | 95.0 | °C | ISO 306/A50 |
| -- | 80.0 | °C | ISO 306/B50 |
| -- | 82.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-2 | UL 94 | |
| 2.50 mm, ALL | V-0 5VB | UL 94 | |
| 3.00 mm, ALL | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 190 - 220 | °C | |
| Front Temperature | 190 - 220 | °C | |
| Nozzle Temperature | 190 - 220 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Back Pressure | 0.490 - 0.981 | MPa | |
| Cushion | 3.18 | mm |
| Injection instructions |
|---|
| Injection Pressure: 50 to 80%Holding Pressure: 20 to 50% |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 速率 A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP271T | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| MOSTEN TB 003 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Unichem 8634 | Colorite Polymers | PVC, Unspecified | Unichem |
| Niretan A F30 AE/V0 | Soredi S.p.a. | Nylon 66 | Niretan A |
| Pebax® 5533 SD 01 | Arkema | PEBA-Ether | Pebax® |