| 50 % Long glass fiber reinforced, heat stabilized, Nylon 6/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 - 0.15 | % | ASTM D955 |
| Transverse flow | 0.15 - 0.25 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 19800 | MPa | ASTM D638 |
| 23°C | 18300 | MPa | ASTM D638 |
| 149°C | 12400 | MPa | ASTM D638 |
| -- | 17000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 343 | MPa | ASTM D638 |
| Fracture, 23°C | 299 | MPa | ASTM D638 |
| Fracture, 149°C | 153 | MPa | ASTM D638 |
| Fracture | 265 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 2.1 | % | ASTM D638 |
| Fracture, 23°C | 2.2 | % | ASTM D638 |
| Fracture, 149°C | 2.4 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus | ISO 178 | ||
| 23°C | 15000 | MPa | ISO 178 |
| 80°C | 9000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 415 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 34 | kJ/m² | ISO 179/1eA |
| 23°C | 47 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 256 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 249 | °C | ISO 75-2/C |
| Melting Temperature 1 | 261 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 285 - 295 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 300 - 310 | °C | |
| Nozzle Temperature | 300 - 315 | °C | |
| Processing (Melt) Temp | 300 - 315 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 300 to 315°CFeed Temperature: 20 to 50°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-332 | Matrix Polymers | LDPE | REVOLVE® |
| Network Polymers PP PPB 25 1202 TF20 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Nymax™ GF1200 A30 FR BK116 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Karina WHITE PVC COMPOUND -E TR-556D10/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ QFP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |