Petrothene® NA345
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3kPEhq_Petrothene-NA345.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA 345 is a series of homopolymer resins that combine premium clarity with strength and stiffness. In addition, NA 345 exhibits good impact strength on both flat and creased film. NA 345 is recommended for textile packaging, light produce, bread bags and other thin packaging films enhanced by clarity and sparkle. The optical values of NA 345 actually improve with decreases in film gauge and are maintained at wide die gap settings. This fact leads to important cost savings. Film can be drawn down to a minimum gauge consistent with required physical properties, with the assurance that optical properties will not suffer, but improve. With wider die gaps back pressures are reduced, as are extrusion costs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm | 179 | MPa | |
| 1% Secant, TD : 32 µm | 207 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 11.0 | MPa | |
| MD : Break, 32 µm | 27.6 | MPa | |
| TD : Break, 32 µm | 23.4 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm | 300 | % | |
| TD : Break, 32 µm | 500 | % | |
| Dart Drop Impact (32 µm) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 360 | g | |
| TD : 32 µm | 200 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® RG-20140 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| TOTAL Polyethylene Lumicene® M 3410 EP (EU) | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Witcobond® 363-02 | Chemtura | PUR-Ether | Witcobond® |
| Formolene® 2302E | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Deprene 151-90 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |