Infino NH-1017
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3iDAVG_InfinoNH1017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NH-1017 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 55 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.20 - 0.30 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.20 - 0.40 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.20 - 0.40 | % | ISO 2577 |
| Traffic : 3.20mm | 0.20 - 0.30 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 113 | ASTM D785 | |
| R scale | 113 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 43.0 | MPa | ASTM D638 |
| Fracture | 44.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 8.8 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2350 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 74.0 | MPa | ASTM D790 |
| -- 8 | 83.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 440 | J/m | ASTM D256 |
| 23°C 10 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 87.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 91.0 | °C | ISO 306/B50 |
| RTI Elec (2.0 mm) | 85.0 | °C | UL 746 |
| RTI Imp (2.0 mm) | 85.0 | °C | UL 746 |
| RTI (2.0 mm) | 85.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.0 to 3.0mm) | V-0 5VB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 4.0 - 6.0 | hr | |
| Hot air dryer | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.040 | % | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 230 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Injection Pressure | 98.0 | MPa | |
| Back Pressure | 1.00 - 2.00 | MPa | |
| Screw Speed | 30 - 50 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC20P105-08FA | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| TechnoDur PBT 4 black (9997) | TechnoCompound GmbH | PBT | TechnoDur |
| XYRON™ X1508 | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| BONDYRAM® 6000 | Polyram Ram-On Industries | ABS | BONDYRAM® |
| Karina BLACK PVC COMP. 809D48/ 1-C-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |