Calsak ABS CS-72
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Calsak Polymers |
| Trademark: | Calsak ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3hna7G_Calsak-ABS-CS-72.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Calsak ABS CS-72 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.18 mm) | 2550 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.18 mm) | 42.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 2620 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.18mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 94.4 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 302 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of injection pressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| 3 . | Type 1 |
| 4 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SM84E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| ExxonMobil™ PP7011L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Ferro PP TPP40AC46BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| KRATON® D1111 K | Kraton Polymers LLC | SIS | KRATON® |
| Karina CLEAR PVC COMPOUND -E 80/298-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |