Bormed™ SC876CF
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormed™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3hGUyQ_Bormed-SC876CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormed SC876CF is a very soft random heterophasic copolymer. This grade is suitable for the manufacturing of non-oriented cast films on chill roll process and blown film on tubular water quenching process. CAS-No. 9010-79-1 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.8 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Injection Molded) | 330 | MPa | ISO 178 |
| Coefficient of Friction | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 180 | MPa | |
| TD : 50 µm | 150 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 40.0 | MPa | |
| TD : Yield, 50 µm | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 680 | % | |
| TD : Break, 50 µm | 720 | % | |
| Instrumented Puncture Test - Total Penetration Energy (50.0 µm) | 650 | J/cm | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 149 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 100 | ASTM D2457 | |
| Haze (50.0 µm) | < 4.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-42234 NAT XRD | Teknor Apex Company | TPE | Medalist® |
| AvaSpire® AV-742 SL30 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| Fiberfil® J-60/10/FR | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Ferro PP LPP30BF05WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Innothane® IE-3068 | Innovative Polymers, Inc. | TSU | Innothane® |