Flexane® Brushable

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Devcon
Trademark:	Flexane®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3hC5vH_Flexane-Brushable.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

A tough, rubber-like urethane compound for making a broad range of repairs to protect against wear, abrasion, and noise reduction.

Intended Use:

Protect equipment surfaces from wear and abrasion.

Protect processing equipment such as coating hoppers, lining chutes, pump volutes, impellers, and fan housings.

Product features:

Bonds with primers to metal, concrete, rubber, wood, and fiberglass

Excellent tear resistance

Mixes easily

Coats up to 50 mils in one pass

Highly resistant to impact and abrasion

General Information
Features	Impact resistance, high Good tear strength Good wear resistance Good toughness
Uses	Repair Materials
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Specific Volume	0.939	cm³/g
Solid content- by Volume	77	%

Mechanical	Nominal Value	Unit	Test Method
Abrasion Loss	90.0	mg/1000 cycles

Thermal	Nominal Value	Unit
Maximum Operating Temperature
Dry	82	°C
Wet	49	°C

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	23	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	86		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength	24.1	MPa	ASTM D412
Tensile Elongation (Break)	600	%	ASTM D412
Tear Strength	70.1	kN/m	ASTM D624

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	13	kV/mm	ASTM D149

Thermoset	Nominal Value	Unit
Thermoset Components
Resin	Mixing ratio by weight: 80
Hardening method	Mixing ratio by weight: 20
Pot Life (24°C)	45	min
Thermoset Mix Viscosity	40000	cP

Additional Information
Cured 7 days @ 75°F

Uncured Properties	Nominal Value	Unit
Curing Time	18	hr

Resin Grade	Manufacturer	Category	Trademark
AMTOPP TL25	Inteplast Group	PP, Unspecified	AMTOPP
Ferro PP LPP40BC15NA	Ferro Corporation	PP Homopolymer	Ferro PP
Kumho PS HFH 407	Korea Kumho Petrochemical Co., Ltd.	PS (IRPS)	Kumho PS
LG PMMA ID193	LG MMA Corp.	Acrylic (PMMA)	LG PMMA
LNP™ THERMOCOMP™ QC006 compound	SABIC Innovative Plastics	Nylon 610	LNP™ THERMOCOMP™