LNP™ THERMOCOMP™ Lexan_LGK3020 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3gzlTh_LNP-THERMOCOMP-Lexan-LGK3020-compound-87833.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP LEXAN_LGK3020 compound is a glass reinforced. Flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Across Flow : 3.20 mm | 0.15 to 0.35 | % | |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 118 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 6580 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 146 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALECCA K-200 | Denka Company Limited | ABS | MALECCA |
| RTP 200 L | RTP Company | Nylon 66 | RTP |
| Xuchuan A-9002/B-6118 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6302 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Plaslube® NY-6/MS/M | Techmer Engineered Solutions | Nylon 12 | Plaslube® |