LG ABS ER400
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3gxBK2_LGABSER400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Description
Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ISO 1133 |
| shrinkage- Flow (3.20 mm) | 0.40 - 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2440 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 52.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress 2 | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 21 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 21 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 4.00 mm) | 85.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 101 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 230 - 240 | °C | |
| Nozzle Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 40 - 60 | °C | |
| Back Pressure | 0.981 - 2.94 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2399 | TECTRON Systems Pte Ltd | TPV | Tectron |
| ACCUTECH™ ABS831G30L | ACLO Compounders Inc. | ABS | ACCUTECH™ |
| Addisil™ 462 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Fluon® PTFE CD145E | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Karina CLEAR PVC COMPOUND 85/227-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |