DIOSHY® TPU T998M
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | DIOSHY Co.,Ltd. |
| Trademark: | DIOSHY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ggmT6_DIOSHY-TPU-T998M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIOSHY® TPU T998M is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) material. It is available in Asia Pacific. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | JIS K7311 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | JIS K7311 | ||
| Shore A | 98 | ||
| Shore D | 53 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | 60.0 | mg | JIS K7311 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 16.7 | MPa | JIS K7311 |
| Tensile Strength | 49.0 | MPa | JIS K7311 |
| Tensile Elongation (Break) | 550 | % | JIS K7311 |
| Compression Set (70°C, 22 hr) | 35 | % | JIS K6301 |
| Rebound Resilience (70°C) | 38 | % | JIS K7311 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 16.7 | MPa | JIS K7311 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -39.0 | °C | DSC |
| Vicat Softening Temperature | 125 | °C | JIS K7206 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo DAP 52-70-70 V0-P | Sumitomo Bakelite North America, Inc. | DAP | Sumitomo DAP |
| TRYCITE™ 8003 | The Dow Chemical Company | PS (HIPS) | TRYCITE™ |
| New-prene™ 7165B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| FLEXCHEM™ 3551-02 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| PLUSTEK PA4802G6BK10 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |