INTEGRAL™ 709
| Category: | Polyolefin, Unspecified , Polyolefin Adhesive Film |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INTEGRAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3gMqrG_INTEGRAL-709.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INTEGRAL™ 709 is a multipurpose, low melt, low viscosity film designed to act as the tie layer between porous substrates, (e.g., fabric to foam adhesion). INTEGRAL 709 is available corona treated (with manufacturing approval). New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative. General Characteristics:
|
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 100 | µm | |
| Film Thickness - Recommended / Available | 2.0-8.0 mil (50-200 µ) | ||
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 51 µm | 107 | MPa | |
| 2% Secant, MD : 100 µm | 86.2 | MPa | |
| 2% Secant, TD : 51 µm | 121 | MPa | |
| 2% Secant, TD : 100 µm | 103 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 9.65 | MPa | |
| MD : Yield, 100 µm | 9.65 | MPa | |
| TD : Yield, 51 µm | 8.27 | MPa | |
| TD : Yield, 100 µm | 8.27 | MPa | |
| MD : Break, 51 µm | 19.7 | MPa | |
| MD : Break, 100 µm | 19.7 | MPa | |
| TD : Break, 51 µm | 12.4 | MPa | |
| TD : Break, 100 µm | 11.7 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 51 µm | 200 | % | |
| MD : Break, 100 µm | 350 | % | |
| TD : Break, 51 µm | 400 | % | |
| TD : Break, 100 µm | 350 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 30 | g | |
| MD : 100 µm | 80 | g | |
| TD : 51 µm | 250 | g | |
| TD : 100 µm | 500 | g | |
| Film Width | 30.48 to 193.04 | cm | |
| Yield (25.0 µm) | 41.9 | m²/kg |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Activation Temperature | 85 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SBB4707 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TRANSMARE® 9RCGF30-1.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Durethan® B 30 S FN30 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Karina GRAY PVC COMPOUND -E800-18/258-CR-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| StarClear® 1050-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarClear® |