HiFill® PC / PET 2230 HF UV
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3gAASQ_HiFill-PC-PET-2230-HF-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PC / PET 2230 HF UV is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 260°C/2.16 kg | 8.0 | g/10 min | |
| 275°C/1.0 kg | 13 | g/10 min | |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.17 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 129 | °C | |
| 1.8 MPa, Unannealed | 121 | °C | |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 238 to 266 | °C | |
| Middle Temperature | 238 to 266 | °C | |
| Front Temperature | 238 to 266 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 54.4 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.414 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics DC-491 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| 4LAC® 10H20000 A-M | 4Plas | ABS | 4LAC® |
| Axiall PVC 11850 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Elastollan® 1185A50X | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| PLEXIGLAS® Film 0F016 | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |