Generic PEEK - Carbon Fiber
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3fBAtY_Generic-PEEK---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PEEK - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.33 - 1.54 | g/cm³ | ASTM D792 |
| 23°C | 1.34 - 1.48 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (380°C/10.0 kg) | 8.00 - 61.3 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.036 - 0.22 | % | ASTM D955 |
| Transverse flow : 23°C | 0.52 - 1.1 | % | ASTM D955 |
| 23°C | 0.12 - 0.62 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.062 - 0.15 | % | ASTM D570 |
| 23°C, 24 hr | 0.098 - 0.10 | % | ISO 62 |
| Saturated, 23°C | 0.29 - 0.41 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.093 - 0.31 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 105 - 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 7010 - 43900 | MPa | ASTM D638 |
| 23°C | 9400 - 27000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 184 - 270 | MPa | ASTM D638 |
| Yield, 23°C | 130 - 242 | MPa | ISO 527-2 |
| Fracture, 23°C | 136 - 284 | MPa | ASTM D638 |
| Fracture, 23°C | 144 - 324 | MPa | ISO 527-2 |
| 23°C | 145 - 318 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.3 - 2.6 | % | ASTM D638 |
| Yield, 23°C | 1.3 - 3.3 | % | ISO 527-2 |
| Fracture, 23°C | 0.93 - 2.5 | % | ASTM D638 |
| Fracture, 23°C | 1.2 - 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 7810 - 31700 | MPa | ASTM D790 |
| 23°C | 5850 - 37300 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 212 - 435 | MPa | ASTM D790 |
| 23°C | 192 - 462 | MPa | ISO 178 |
| Compressive Strength | |||
| 23°C | 170 - 1360 | MPa | ASTM D695 |
| 23°C | 49.0 - 303 | MPa | ISO 604 |
| Shear Strength (23°C) | 95.3 - 122 | MPa | ASTM D732 |
| Coefficient of Friction | 0.12 - 0.35 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 - 61 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 53 - 110 | J/m | ASTM D256 |
| 23°C | 6.4 - 9.1 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 380 - 920 | J/m | ASTM D256 |
| 23°C | 29 - 61 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 4.40 - 17.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 288 - 340 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 298 - 350 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 287 - 317 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 260 - 332 | °C | ISO 75-2/A |
| Continuous Use Temperature | 248 - 251 | °C | ASTM D794 |
| Vicat Softening Temperature | 295 - 340 | °C | ISO 306 |
| Melting Temperature | 340 - 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 1.9E-6 - 3.2E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.0E-6 - 5.2E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.0E-6 - 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.2E-6 - 5.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 3.9E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.45 - 0.99 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 50 - 1.3E+5 | ohms | ASTM D257 |
| -- | 1.0E+2 - 2.5E+10 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.4E-5 - 2.5E+5 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+3 - 2.5E+7 | ohms·cm | IEC 60093 |
| Insulation Resistance (23°C) | 1.0E+2 - 2.5E+10 | ohms | IEC 60167 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 200 - 920 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 152 | °C | |
| Drying Time | 3.0 - 7.0 | hr | |
| Dew Point | -28.9 | °C | |
| Suggested Max Moisture | 0.099 - 0.10 | % | |
| Rear Temperature | 365 - 366 | °C | |
| Middle Temperature | 373 - 385 | °C | |
| Front Temperature | 373 - 396 | °C | |
| Nozzle Temperature | 370 - 371 | °C | |
| Processing (Melt) Temp | 371 - 390 | °C | |
| Mold Temperature | 178 - 192 | °C | |
| Injection Pressure | 102 - 103 | MPa | |
| Back Pressure | 0.500 - 0.519 | MPa | |
| Screw Speed | 55 - 80 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PEEK - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2570F | Teknor Apex Company | TPE | Telcar® |
| Yuyao PP TL303 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Chemlon® 109-18 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| LUVOCOM® 21-8115 | Lehmann & Voss & Co. | Nylon 6/6T | LUVOCOM® |
| Sylvin 4200-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |