Network Polymers PP PPB 25 1316
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3el0NU_Network-Polymers-PP-PPB-25-1316.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Network Polymers PP PPB 25 1316 is a Polypropylene Copolymer (PP Copolymer) product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 7.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 110 | J/m | |
| 23°C, 3.18 mm | 590 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 97.2 | °C | |
| 1.8 MPa, Unannealed | 51.1 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 33 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound G3230AE | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PPcompound |
| Zythane® 8090AM | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| ASI POLYETHYLENE CP 851 | A. Schulman Inc. | LDPE | ASI POLYETHYLENE |
| Interpol 47-5138/47-5205 | Cook Composites and Polymers | PUR-Ester | Interpol |
| MAJORIS EW850 | AD majoris | PP, Unspecified | MAJORIS |