G-PAEK™ 1215GF
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | G-PAEK™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ePdcI_G-PAEK-1215GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra High Performance Thermoplastic polymer, 15% glass fiber reinforced in Polyether Ketone, semi-crystalline granules suitable for injection molding, easy flow, light beige in color and also custom colors in Blue and Black. Application Areas: Suitable for high temperature application, where higher strength in load-bearing applications. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | |
| Molding Shrinkage 1 | |||
| Flow | 1.0 | % | |
| Across Flow | 1.3 | % | |
| Water Absorption (Equilibrium) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ASTM D785 | |
| Durometer Hardness (Shore D) | 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7800 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.8 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7.70 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 33 | J/m | ASTM D256 |
| Unnotched Izod Impact | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 348 | °C | ASTM D648 |
| Continuous Use Temperature | 280 | °C | UL 746B |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Melting Temperature | 372 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 410 | °C | |
| Processing (Melt) Temp | 390 to 410 | °C | |
| Mold Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 410°C nozzle, 220°C Mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 65215 | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Stanyl® ForTii™ F12 | DSM Engineering Plastics | Nylon 4T | Stanyl® ForTii™ |
| THERMOLAST® K TC8LEZ (Series: UV/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Emulprene® 1006 | INSA | SBR, Emulsion | Emulprene® |
| MACOMASS PP MM-PP HG 23 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |