INEOS HDPE B53-35H-011
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3cvMcg_INEOS-HDPE-B53-35H-011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| B53-35H-011 is a high density polyethylene copolymer developed for blow molding applications. This product is recommended for use in applications which require a combination of high top load strength and good environmental stress crack resistance (ESCR). This material meets the Food and Drug Administration requirements of 21CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, F50) | 30.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 27.6 | MPa | |
| Break | 17.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.0 | % | |
| Break | > 600 | % | |
| Flexural Modulus | ASTM D790A | ||
| 2% Secant | 1030 | MPa | |
| Tangent | 1450 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 170 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | 16.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 75.0 | °C | |
| 1.8 MPa, Unannealed | 47.8 | °C | |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3640B | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Salflex 830I | Salflex Polymers Ltd. | PP, Unspecified | Salflex |
| Sylvin 9610-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Kotex K-30FRT12 | Kotec Corporation | PC | Kotex |
| OTECH CPE XLO9141 - Cable Jacket | OTECH Corporation | CPE | OTECH CPE |