Order Products : sales@su-jiao.com
MonoSol® AF L711 Blue 40µ
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3bsYZc_MonoSol-AF-L711-Blue-40-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol AF L711 Blue is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF L711 Blue is a grade of PVOH cold water-soluble packaging film engineered for flow wrapping and pleat wrapping of tablets. This film has excellent stiffness for ease of processing on flow wrapping and pleat wrapping equipment. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 6.7 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 40.0 µm | 16.0 | sec | |
| Disintegration : 24°C, 40.0 µm | 10.0 | sec | |
| Dissolution : 10°C, 40.0 µm | 74.0 | sec | |
| Dissolution : 24°C, 40.0 µm | 58.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (40.0 µm) | 20.1 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 20 µm to 60 µm | ||
| Secant Modulus | ASTM D882, ISO 527-3 | ||
| 10%, MD : 40 µm | 101 | MPa | |
| 100%, MD : 40 µm | 37.2 | MPa | |
| 10%, TD : 40 µm | 76.5 | MPa | |
| 100%, TD : 40 µm | 16.5 | MPa | |
| Tensile Strength | |||
| MD : Break, 40 µm | 51.0 | MPa | ASTM D882 |
| TD : Break, 40 µm | 40.7 | MPa | ASTM D882 |
| MD : 40 µm | 51.0 | MPa | ISO 527-3 |
| TD : 40 µm | 40.7 | MPa | ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Break, 40 µm | 190 | % | |
| TD : Break, 40 µm | 330 | % | |
| Elmendorf Tear Strength | |||
| MD : 40 µm | 1400 | g | ASTM D1922 |
| TD : 40 µm | 1200 | g | ASTM D1922 |
| MD : 40 µm | 0.14 | N | ISO 6383-2 |
| TD : 40 µm | 0.12 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8253 HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| NOVADURAN® 5010R8M | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Hifax TRC 103P R299 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Karina WHITE COLOR CONCENTRATE 10/ 96-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8980-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |